Kinetics of Secondary Recrystallization in Grain-Oriented Silicon Steel Based on Grain Size Distribution

Abstract

Quasi in situ observations of the early stage of secondary recrystallization in Fe-3.25 wt.% Si high-permeability grain-oriented silicon steel indicate that large matrix grains locally impede the migration of secondary recrystallized grain boundaries. A critical grain-size criterion for identifying potential pinning grains is proposed, and a kinetic model incorporating the matrix grain-size distribution is developed. For the abnormal grain tracked at 1000 °C, the measured grain-size increment over 100 s was approximately 60 μm; the proposed pinning model predicted 47 μm, whereas the weighted-average model predicted 171 μm. Model calculations further suggest that matrix grain-size dispersion, pinning force, grain size, and relative grain-boundary energy jointly affect the early-stage growth of Goss grains. These results provide a framework for interpreting early secondary-recrystallization kinetics, while broader experimental validation is still required before the predicted parameter combinations can be used for process control.