Vacuum-Compatible Electrode-Free Poling of PVDF Films Using Glow-Discharge Plasma

Abstract

Glow-discharge plasma (GDP) poling is revisited as an electrode-free method for activating piezoelectricity in poly(vinylidene fluoride) (PVDF) films. Although this method was proposed several decades ago, its effect on the properties of PVDF films has remained poorly understood. In this work, we demonstrate that GDP enables efficient poling of oriented PVDF films without pre-deposited electrodes and investigate the relationship between plasma treatment time, structural evolution, and piezoelectric response. Commercially available 25 μm-thick oriented PVDF films (PolyK) were treated in a DC glow discharge for 15 s to 15 min and characterized using FTIR, DSC, piezoresponse force microscopy, UV–Vis–NIR spectrophotometry, quasi-static d33 measurements and water contact-angle measurements. GDP poling produced a side-averaged piezoelectric coefficient d33 of up to ~25 pC/N within 1–5 min, with local maxima at approximately 1, 2.5, and 5 min. This behavior was accompanied by pronounced changes in the domain structure, including an increase in the ferroelectric domain size from 86 to 552 nm, while the crystallinity and electroactive phase fraction changed only moderately. Plasma treatment also increased the wettability of the plasma-facing surface, reducing the water contact angle from about 85° to 42° within 3 min. At longer treatment times (>5 min), however, the piezoelectric response decreased and the optical transparency deteriorated because of increased haze and turbidity, most likely associated with plasma-induced chemical modification of the surface layers. These results indicate that GDP poling has an effective processing window of 1–5 min. The proposed approach provides a vacuum-compatible and electrode-free route for preparing PVDF films with increased surface wettability for flexible piezoelectric sensors, wearable electronics, and integrated polymer-based devices, because it is compatible with electrode deposition on an already activated polymer surface within a single vacuum cycle.